SAP Material Number 1849276
ISO Catalog Number KCGR110308R08
ANSI Catalog Number NPGR52R
Grade KC5010
[LI] Insert Length 9.525
[LI] Insert Length .3750
[L10] Insert Cutting Edge Length 11.597
[L10] Insert Cutting Edge Length .4566
[W] Insert Width 6.350
[W] Insert Width .2500
[S] Insert Thickness 3.180
[S] Insert Thickness .1250
[M] Gage Dimension 8.660
[M] Gage Dimension .3409
[Rε] Corner Radius 0.800
[Rε] Corner Radius .0312
See all Product Variants

Workpiece Material

P
M
K
N
S
H

Grades

  • K68

    Composition: A hard, low binder content, alloyed grade WC/Co fine-grain grade.
    Application: The K68 grade has excellent abrasion resistance for machining cast irons, austenitic stainless steels, non-ferrous metals, non-metals, and as an alternative to the K313 grade on most high-temperature alloys. Use as a general-purpose grade for non-ferrous materials.

    S
    N
  • KC5010

    Composition: An advanced PVD AlTiN coating over a very deformation-resistant unalloyed carbide substrate. The new and improved coating enables speeds to be increased by 50–100%.
    Application: The KC5010 grade is ideal for finishing to general machining of most workpiece materials at higher speeds. Excellent for machining most steels, stainless steels, cast irons, non-ferrous materials, and super alloys under stable conditions. It also performs well machining hardened and short chipping materials.

    P
    S
    H
    K
    M
    N
  • KC5025

    Composition: An advanced PVD-AlTiN-coated grade with a tough, ultra-fine-grain unalloyed substrate.
    Application: For general-purpose machining of most steels, stainless steels, high-temp alloys, titanium, irons, and non-ferrous materials. Speeds may vary from low to medium and will handle interruptions and high feed rates.

    P
    S
    K
    M
    N
  • KC5410

    Composition: A PVD TiB2 coating over a very deformation-resistant unalloyed substrate.
    Application: Designed for roughing, semi-finishing, and finishing of free machining (hypoeutectic <12,2% Si) aluminium, aluminium alloys, and magnesium alloys. The TiB2 coating is harder than TiN and TiAlN coatings and has an extremely smooth surface, resulting in reduced surface friction, speedy chip flow, and outstanding wear resistance. Built-up edge is prevented because this coating has a very low affinity for aluminium. The substrate is unalloyed and fine grained and offers sharp edges, smooth surfaces, and excellent thermal deformation resistance and edge integrity. Inserts with a ground periphery are polished before coating and have a sharp edge. Moulded inserts have a light hone.

    N
  • KCM15B

    Composition: A multilayer MTCVD-TiCN-Al2O3 coated carbide grade.

    Application: An excellent finishing to medium machining grade for austenitic stainless steels at higher speeds and covers a broad range of steel applications in the P20-25 range. KCM15 grade in combination with unique geometries have been designed to resist depth-of-cut notching and minimize burr formation. The post-coat treatment reduces coating stresses, improves coating adhesion, minimizes microchipping and edge build-up, and improves workpiece finish.

  • KCP10B

    Composition: A specially engineered cobalt-enriched carbide grade with thick MTCVD-TiCN-Al2O3-TiOCN coating for maximum wear resistance.

    Application: An excellent finishing to medium machining grade for a variety of workpiece materials, including most steels, ferritic, martensitic, and PH stainless steels, and cast irons. The cobalt-enriched substrate offers a balanced combination of deformation resistance and edge toughness, while the thick coating layers offer outstanding abrasion resistance and crater wear resistance for high-speed machining. Smooth coating provides resistance to edge build-up and microchipping and produces excellent surface finishes.

    P
    K
  • KCU10

    Composition: An advanced multilayer PVD coating over a very deformation-resistant unalloyed carbide substrate. The new and improved coating improves edge stability with wide range speed and feed capabilities.
    Application: The KCU10 grade is ideal for finishing to general machining of most workpiece materials at a wide range of speed and feed capabilities. Excellent for machining most steels, stainless steels, cast irons, non-ferrous materials, and super alloys with improved edge toughness and higher cutting speed/feed capability.

    P
    S
    H
    K
    M
    N
  • KCU25

    Turning Composition: An advanced PVD grade with hard AlTiN coating and fine-grain unalloyed substrate. The new and improved coating improves edge stability with wide range speed and feed capabilities.

    Turning Application: The KCU25 grade is ideal for general machining of most steels, stainless steels, high-temp alloys, titanium, irons, and non-ferrous materials in a wide range of speeds and feeds with improved edge toughness for interrupted cut and high feed rates.

    Holemaking Composition: Advanced CVD TiCN-Al2O3 coating combined with a tough carbide substrate.

    Holemaking Application: First choice for steel, stainless steel, and cast iron. This grade offers adequate deformation resistance, excellent edge strength, and superior wear resistance over a wide range of machining conditions for high productivity with very good reliability.

    P
    S
    K
    M
    N
  • KD100

    composition: A polycrystalline diamond tip (PCD) brazed onto a
    carbide substrate.
    application: The KD100 grade is for general purpose turning. The
    cutting tool material contains a binder in addition to diamond
    particles. This makes the KD100 grade suitable for roughing to
    finishing all types of highly abrasive workpieces, including non-ferrous
    metals and non-metallics. Use as your first choice on high content
    silicon aluminum alloys (hypereutectic). Will generally produce good
    surface finishes. Provides the best mechanical shock resistance of the
    diamond tool materials. The cutting edge is sharp. This grade operates
    at very high speeds.

  • KD1425

    Composition: A multimodal PCD grade with a range of grain sizes brazed onto a carbide substrate.
    Application: Engineered for extreme abrasion resistance, combined with good edge strength for demanding applications. An ideal choice for high-silicon aluminium alloys, bi-metallic (AL/GCI) materials, MMC, carbon-fibre reinforced plastics, and other abrasive non-metallic materials.

    N
  • KT125

    KT125

  • KT315

    Composition: A multilayer PVD-TiN/TiCN/TiN-coated cermet turning grade.
    Application: Ideal for high-speed finishing to medium machining of most carbon and alloy steels and stainless steels. Performs very well in cast and ductile iron applications, too. Provides long and consistent tool life and will produce excellent workpiece finishes.

    P
    M