CNGP

Grades

• 
  K10U

  Coated carbide. PVD-TiAlN-TiN. Ideal for finishing of difficult-to-machine alloys and stainless steels.

  P Steel

  S High-Temp Alloys

  M Stainless Steel
• 
  K15U

  Uncoated carbide. Excellent abrasion resistance for machining cast irons, austenitic stainless steels, and most high-temperature alloys.
  Coatings provide high-speed capability and are engineered for finishing to heavy roughing.

  S High-Temp Alloys

  N Non-Ferrous
• 
  K313

  Composition: A hard, low binder content, unalloyed WC/Co fine-grain grade.
  Application: Exceptional edge wear resistance combined with very high strength for machining titanium, cast irons, austenitic stainless steels, non-ferrous metals, non-metals, and most high-temp alloys. Superior thermal deformation and depth-of-cut notch resistance. The grain structure is well controlled for minimal pits and flaws, which contributes to long, reliable service.

  S High-Temp Alloys

  N Non-Ferrous
• 
  K68

  Composition: A hard, low binder content, alloyed grade WC/Co fine-grain grade.
  Application: The K68 grade has excellent abrasion resistance for machining cast irons, austenitic stainless steels, non-ferrous metals, non-metals, and as an alternative to the K313 grade on most high-temperature alloys. Use as a general-purpose grade for non-ferrous materials.

  S High-Temp Alloys

  N Non-Ferrous
• 
  KC5010

  Composition: An advanced PVD AlTiN coating over a very deformation-resistant unalloyed carbide substrate. The new and improved coating enables speeds to be increased by 50–100%.
  Application: The KC5010 grade is ideal for finishing to general machining of most workpiece materials at higher speeds. Excellent for machining most steels, stainless steels, cast irons, non-ferrous materials, and super alloys under stable conditions. It also performs well machining hardened and short chipping materials.

  P Steel

  S High-Temp Alloys

  M Stainless Steel
• 
  KC5410

  • TiB2-PVD coating over a very deformation-resistant unalloyed substrate.
  
  
  • Designed for roughing, semifinishing, and finishing of free machining (hypoeutectic <12,2% Si) aluminum, aluminum alloys, and magnesium alloys.
  
  
  • High hardness and extremely smooth surface, resulting in reduced surface friction, speedy chip flow, and outstanding wear resistance.
  
  
  • Prevents built-up edge because of a very low affinity for aluminum.

  N Non-Ferrous
• KC730

  KC730

  P Steel

  S High-Temp Alloys

  M Stainless Steel
• KC7310

  PVD-TiAIN coated, unalloyed carbide
  Good Wear resistance
  High level of resistance against plastic deformation
  Smaller rounded edges in comparison with CVD grades
  Recommended finishing grade for stainless steel
  
  
  

• KC732

  KC732

• 
  KCU10

  Composition: An advanced multilayer PVD coating over a very deformation-resistant unalloyed carbide substrate. The new and improved coating improves edge stability with wide range speed and feed capabilities.
  
  Application: The KCU10™ grade is ideal for finishing to general machining of most workpiece materials at a wide range of speed and feed capabilities. Excellent for machining most steels, stainless steels, cast irons, non-ferrous materials, and super alloys with improved edge toughness and higher cutting speed/feed capability.

  P Steel

  S High-Temp Alloys

  M Stainless Steel