Screw-On Inserts
Screw-On Inserts
Screw-On Inserts
Screw-On Inserts

ISO Carbide Inserts

Screw-On Inserts

Metric
Inch
SAP Material Number 1871020
ISO Catalog Number DCMT150404LF
ANSI Catalog Number DCMT431LF
Grade KC5010
[D] Insert IC Size 12.7000
[D] Insert IC Size .5000
[L10] Insert Cutting Edge Length 15.5040
[L10] Insert Cutting Edge Length .6104
[S] Insert Thickness 4.7600
[S] Insert Thickness .1875
[Rε] Corner Radius 0.4000
[Rε] Corner Radius .0156
[D1] Insert Hole Size 5.5000
[D1] Insert Hole Size .2165
See all Product Variants

Workpiece Material

P
M
S

Features and benefits

  • Finishing geometry with light cutting action.

  • Used in multiple material groups.

  • Beyond™ Drive™ grades included.

Grades

  • K313

    Composition: A hard, low binder content, unalloyed WC/Co fine-grain grade.
    Application: Exceptional edge wear resistance combined with very high strength for machining titanium, cast irons, austenitic stainless steels, non-ferrous metals, non-metals, and most high-temp alloys. Superior thermal deformation and depth-of-cut notch resistance. The grain structure is well controlled for minimal pits and flaws, which contributes to long, reliable service.

    S
    N
  • K68

    Composition: A hard, low binder content, alloyed grade WC/Co fine-grain grade.
    Application: The K68 grade has excellent abrasion resistance for machining cast irons, austenitic stainless steels, non-ferrous metals, non-metals, and as an alternative to the K313 grade on most high-temperature alloys. Use as a general-purpose grade for non-ferrous materials.

    S
    N
  • KC5010

    Composition: An advanced PVD AlTiN coating over a very deformation-resistant unalloyed carbide substrate. The new and improved coating enables speeds to be increased by 50–100%.
    Application: The KC5010 grade is ideal for finishing to general machining of most workpiece materials at higher speeds. Excellent for machining most steels, stainless steels, cast irons, non-ferrous materials, and super alloys under stable conditions. It also performs well machining hardened and short chipping materials.

    P
    S
    M
  • KC5025

    Composition: An advanced PVD-AlTiN-coated grade with a tough, ultra-fine-grain unalloyed substrate.
    Application: For general-purpose machining of most steels, stainless steels, high-temp alloys, titanium, irons, and non-ferrous materials. Speeds may vary from low to medium and will handle interruptions and high feed rates.

    S
    M
  • KCK05

    Composition: A multilayered coating with moderately thick MTCVD TiCN-Al2O3 layers over a highly deformation-resistant carbide substrate.
    Application: Designed for high-speed machining of grey and ductile irons. The substrate and coating architecture together with CW5 post-coat treatment ensure a tremendous tool life advantage, especially when cutting higher tensile strength ductile and grey irons where workpiece size consistency and reliability of tool life are critical. Excellent both in straight and varied depths of cut.

    P
    K
  • KCK05B

    Composition: A multilayered coating with moderately thick MTCVD TiCN-Al2O3-TiOCN layers over a highly deformation-resistant carbide substrate.

    Application: Designed for high-speed machining of gray and ductile irons. The substrate and coating architecture together with CW5 post-coat treatment ensure a tremendous tool life advantage, especially when cutting higher tensile strength ductile and gray irons where workpiece size consistency and reliability of tool life are critical. Excellent both in straight and varied depths of cut.

    P
    K
  • KCK15

    Composition: A multilayered coating with thick MTCVD TiCN-Al2O3 layers applied over a carbide substrate specifically engineered for cast irons.
    Application: Delivers consistent performance in high-speed machining of grey and ductile irons. The substrate design permits the insert to stay in the cut for a long time at high speeds with minimum deformation. The thick CVD coating and post-coat treatment provide superior wear resistance ensuring long and consistent tool life. Can be applied both in straight and lightly interrupted cuts.

    P
    K
  • KCK15B

    Composition: A multilayered coating with thick MTCVD TiCN-Al2O3-TiOCN layers applied over a carbide substrate specifically engineered for cast irons.

    Application: Delivers consistent performance in high-speed machining of gray and ductile irons. The substrate design permits the insert to stay in the cut for a long time at high speeds with minimum deformation. The thick CVD coating and post-coat treatment provide superior wear resistance ensuring long and consistent tool life. Can be applied both in straight and lightly interrupted cuts.

    P
    K
  • KCK20

    Composition: A specially toughened MTCVD-TICN-Al2O3 coating over a wear-resistant substrate.
    Application: The KCK20 grade is specifically engineered to maximise coating adhesion and edge strength making this grade ideal in wet interrupted cutting of grey and ductile irons. It can be used in a wide range of applications from finishing to roughing to maximise productivity wherever strength and reliability are needed.

    P
    K
  • KCK20B

    Composition: A specially toughened MTCVD-TICN-Al2O3-TiOCN coating over a wear-resistant substrate.

    Application: The KCK20 grade is specifically engineered to maximize coating adhesion and edge strength making this grade ideal in wet interrupted cutting of gray and ductile irons. It can be used in a wide range of applications from finishing to roughing to maximize productivity wherever strength and reliability are needed.

    P
    K
  • KCM15

    Composition: A multilayer MTCVD-TiCN-Al2O3 coated carbide grade.
    Application: An excellent finishing to medium machining grade for austenitic stainless steels at higher speeds and covers a broad range of steel applications in the P20–25 range. KCM15 grade in combination with unique geometries have been designed to resist depth-of-cut notching and minimise burr formation. The post-coat treatment reduces coating stresses, improves coating adhesion, minimises microchipping and edge build-up, and improves workpiece finish.

    P
    S
    M
  • KCM15B

    Composition: A multilayer MTCVD-TiCN-Al2O3 coated carbide grade.

    Application: An excellent finishing to medium machining grade for austenitic stainless steels at higher speeds and covers a broad range of steel applications in the P20-25 range. KCM15 grade in combination with unique geometries have been designed to resist depth-of-cut notching and minimize burr formation. The post-coat treatment reduces coating stresses, improves coating adhesion, minimizes microchipping and edge build-up, and improves workpiece finish.

    P
    S
    M
  • KCM25

    Composition: A multilayer CVD coating comprised of TiN-MT-TiCN-Al2O3 layers over a tough, cobalt-enriched carbide substrate.
    Application: This CVD-coated grade is designed for general-purpose machining of austenitic stainless steels at moderate speeds and feeds. KCM25 inserts offer an extraordinary combination of toughness, built-up edge resistance, and wear resistance in stainless steel applications.

    P
    S
    M
  • KCM25B

    Composition: A multilayer MTCVD-TiCN-Al2O3-TiOCN coated carbide grade.

    Application: An excellent finishing to medium machining grade for austenitic stainless steels at higher speeds and covers a broad range of steel applications in the P20-25 range. KCM15 grade in combination with unique geometries have been designed to resist depth-of-cut notching and minimize burr formation. The post-coat treatment reduces coating stresses, improves coating adhesion, minimizes microchipping and edge build-up, and improves workpiece finish.

    P
    S
    M
  • KCM35

    Composition: A multilayer TiN-MT-TiCN-Al2O3 CVD coating over a super-tough substrate.
    Application: The KCM35 grade is engineered to take on the most brutal cast stainless steel machining applications. The substrate withstands heavy interruptions, while the coating provides the wear resistance needed for long tool life. The polished surface resists edge build-up, even at slow cutting speeds. KCM35 grade is available in insert sizes and geometries appropriate for heavy feeds and large depths of cut.

    P
    S
    M
  • KCM35B

    Composition: A multilayer TiN-MT-TiCN-Al2O3-TiOCN CVD coating over a super-tough substrate.

    Application: The KCM35 grade is engineered to take on the most brutal cast stainless steel machining applications. The substrate withstands heavy interruptions, while the coating provides the wear resistance needed for long tool life. The polished surface resists edge build-up, even at slow cutting speeds. KCM35 grade is available in insert sizes and geometries appropriate for heavy feeds and large depths of cut.

    P
    S
    M
  • KCP05

    Composition: An innovative, highly deformation-resistant, cobalt-enriched substrate with a specially designed, adherent MTCVD-TiCN-Al2O3 coating.
    Application: For finishing to semi-finishing of most steels, ferritic, martensitic, and PH stainless steels and cast irons. Provides excellent combination of deformation resistance and insert edge strength. The new coating combined with a state-of-the-art post-coat treatment provides high-productivity with long predictable tool life and superior workpiece surface finish.

    P
    K
  • KCP10

    Composition: A specially engineered cobalt-enriched carbide grade with thick MTCVD-TiCN-Al2O3 coating for maximum wear resistance.
    Application: An excellent finishing to medium machining grade for a variety of workpiece materials, including most steels, ferritic, martensitic, and PH stainless steels, and cast irons. The cobalt-enriched substrate offers a balanced combination of deformation resistance and edge toughness, while the thick coating layers offer outstanding abrasion resistance and crater wear resistance for high-speed machining. Smooth coating provides resistance to edge build-up and microchipping and produces excellent surface finishes.

    P
    K
  • KCP10B

    Composition: A specially engineered cobalt-enriched carbide grade with thick MTCVD-TiCN-Al2O3-TiOCN coating for maximum wear resistance.

    Application: An excellent finishing to medium machining grade for a variety of workpiece materials, including most steels, ferritic, martensitic, and PH stainless steels, and cast irons. The cobalt-enriched substrate offers a balanced combination of deformation resistance and edge toughness, while the thick coating layers offer outstanding abrasion resistance and crater wear resistance for high-speed machining. Smooth coating provides resistance to edge build-up and microchipping and produces excellent surface finishes.

    P
    K
  • KCP25

    Composition: A tough cobalt-enriched carbide grade with a newly designed multilayer MTCVD-TiCN-Al2O3 coating with superior interlayer adhesion.
    Application: Best general-purpose turning grade for most steels and ferritic and martensitic stainless steels. The substrate design ensures adequate deformation resistance with excellent insert edge strength. Coating layers offer good wear resistance over a wide range of machining conditions and the post-coat treatment minimises microchipping and improves coating adhesion to substrate leading to long tool life and improved workpiece finishes.

    P
    K
  • KCP25B

    Composition: A tough cobalt-enriched carbide grade with a newly designed multilayer MTCVD-TiCN-Al2O3-TiOCN coating with superior interlayer adhesion.

    Application: Best general-purpose turning grade for most steels and ferritic and martensitic stainless steels. The substrate design ensures adequate deformation resistance with excellent insert edge strength. Coating layers offer good wear resistance over a wide range of machining conditions and the post-coat treatment minimises microchipping and improves coating adhesion to substrate leading to long tool life and improved workpiece finishes.

    P
    K
  • KCP30

    Composition: A newly engineered, tough cobalt-enriched carbide grade with an advanced multilayer TiN-MT-TiCN-Al2O3 coating.
    Application: For medium to rough machining of all carbon, alloy, and stainless steels. The substrate design provides superior insert strength that is required for this application, and the multilayer coating adds wear resistance to the insert resulting in long tool life.

    P
  • KCU10

    Composition: An advanced multilayer PVD coating over a very deformation-resistant unalloyed carbide substrate. The new and improved coating improves edge stability with wide range speed and feed capabilities.
    Application: The KCU10 grade is ideal for finishing to general machining of most workpiece materials at a wide range of speed and feed capabilities. Excellent for machining most steels, stainless steels, cast irons, non-ferrous materials, and super alloys with improved edge toughness and higher cutting speed/feed capability.

    P
    S
    M
  • KT125

    KT125

  • KT315

    Composition: A multilayer PVD-TiN/TiCN/TiN-coated cermet turning grade.
    Application: Ideal for high-speed finishing to medium machining of most carbon and alloy steels and stainless steels. Performs very well in cast and ductile iron applications, too. Provides long and consistent tool life and will produce excellent workpiece finishes.

    P