Beyond™ RU & UPG Geometries

Pin Clamping

Metric
Inch
SAP Material Number 6320355
ISO Catalog Number RCMT1606M0UPG
ANSI Catalog Number RCMT1606M0UPG
Grade KCP10B
[D] Insert IC Size 16.0000
[D] Insert IC Size .6300
[D1] Insert Hole Size 5.5000
[D1] Insert Hole Size .2170
[S] Insert Thickness 6.3500
[S] Insert Thickness .2500
See all Product Variants

Workpiece Material

P
K

Grades

  • KCK15B

    Composition: A multilayered coating with thick MTCVD TiCN-Al2O3-TiOCN layers applied over a carbide substrate specifically engineered for cast irons.

    Application: Delivers consistent performance in high-speed machining of gray and ductile irons. The substrate design permits the insert to stay in the cut for a long time at high speeds with minimum deformation. The thick CVD coating and post-coat treatment provide superior wear resistance ensuring long and consistent tool life. Can be applied both in straight and lightly interrupted cuts.

    P
    K
  • KCP10B

    Composition: A specially engineered cobalt-enriched carbide grade with thick MTCVD-TiCN-Al2O3-TiOCN coating for maximum wear resistance.

    Application: An excellent finishing to medium machining grade for a variety of workpiece materials, including most steels, ferritic, martensitic, and PH stainless steels, and cast irons. The cobalt-enriched substrate offers a balanced combination of deformation resistance and edge toughness, while the thick coating layers offer outstanding abrasion resistance and crater wear resistance for high-speed machining. Smooth coating provides resistance to edge build-up and microchipping and produces excellent surface finishes.

    P
    K
  • KCP25B

    Composition: A tough cobalt-enriched carbide grade with a newly designed multilayer MTCVD-TiCN-Al2O3-TiOCN coating with superior interlayer adhesion.

    Application: Best general-purpose turning grade for most steels and ferritic and martensitic stainless steels. The substrate design ensures adequate deformation resistance with excellent insert edge strength. Coating layers offer good wear resistance over a wide range of machining conditions and the post-coat treatment minimises microchipping and improves coating adhesion to substrate leading to long tool life and improved workpiece finishes.

    P
    K
  • KCPK05

    Composition: A deformation-resistant, cobalt-enriched substrate combined with thick MTCVD TiCN-Al2O3 coating.

    Application: For high productivity turning of steels and PH stainless steels in continuous to lightly interrupted cuts. This grade provides excellent combination of toughness and high speed wear resistance allowing the fastest steel part production. Its unique combination of substrate and coating also make it an ideal roughing grade for cast iron where chipping resistance is required.

    P