Sold in pkg. of 0
Features and benefits
- Metrische Schraube mit Gewindeausführung gemäß ISO.
Machine Side
loading...
Workpiece Side
loading...
Grades
-
KC610M
Beschichtetes feinkörniges Hartmetall mit harter PVD-Beschichtung (TiCN-TiN), besonders geeignet für sehr verschleißfeste Anwendungen. Nur mit Kühlschmiermittel oder mit Minimalmengenschmierung (MQL) verwenden.
P SteelS High-Temp AlloysK Cast IronM Stainless Steel -
KC620M
Coated carbide grade with a PVD coat (TiN). Coated carbide grade with a PVD coat (TiN). KC620M is suitable for machining cast iron, non-ferrous material, Aluminum alloys. This grade is suitable for both wet and dry machining. suitable for machining cast iron, non-ferrous material, aluminum alloys. This grade is suitable for both wet and dry machining.
TM25 Schnittdatenempfehlung
Materials | Brinell | surface speeds | indexable inserts | |
steel | HB | KC610M | KC635M | feed fz (IPT) |
P1 | 125 | 100–210 | 90–180 | 0,05–0,20 |
P2 | 180 | 100–170 | 90–160 | 0,05–0,20 |
P3 | 225 | 60–130 | 70–115 | 0,05–0,20 |
P4 | 250 | 80–150 | 80–160 | 0,05–0,20 |
P5 | 275 | 75–130 | 80–160 | 0,05–0,15 |
P6 | 325 | 70–110 | 60–100 | 0,05–0,10 |
stainless steel | ||||
M1 | 180 | 100–170 | 120–180 | 0,05–0,10 |
M2 | 250 | 70–140 | 100–140 | 0,05–0,10 |
M3 | 330 | 70–120 | 100–120 | 0,05–0,10 |
cast iron | ||||
K1 | 180 | 60–130 | 100–120 | 0,02–0,08 |
K2 | 220 | 60–125 | 80–100 | 0,05–0,15 |
K3 | 260 | 50–90 | 60–90 | 0,05–0,10 |
non-ferrous | ||||
N1 | 60–100 | 100–250 | – | 0,05–0,25 |
high-temp alloys | ||||
S1 | 200 | 20–45 | 20–40 | 0,05–0,10 |
S2 | 250 | 20–30 | 20–30 | 0,02–0,05 |
S3 | 280 | 15–20 | 15–20 | 0,02–0,05 |
S4 | 350 | 10–15 | 10–15 | 0,02–0,05 |
hardened steel | ||||
H1 | 55 HRC | 20–45 | 20–45 | 0,01–0,03 |
STN Series
Materials | Brinell | surface speeds | indexable inserts | |
steel | HB | KC610M | KC635M | feed fz (IPT) |
P1 | 125 | 325–675 | 290–590 | .002–.008 |
P2 | 180 | 290–550 | 290–520 | .002–.008 |
P3 | 225 | 200–425 | 225–375 | .002–.008 |
P4 | 250 | 250–490 | 250–500 | .002–.008 |
P5 | 275 | 250–425 | 250–500 | .002–.006 |
P6 | 325 | 225–350 | 200–325 | .002–.004 |
stainless steel | ||||
M1 | 180 | 325–550 | 375–590 | .002–.004 |
M2 | 250 | 225–450 | 325–450 | .002–.004 |
M3 | 330 | 225–375 | 325–375 | .002–.004 |
cast iron | ||||
K1 | 180 | 200–425 | 325–450 | .001–.003 |
K2 | 220 | 200–390 | 250–325 | .002–.006 |
K3 | 260 | 160–290 | 200–275 | .002–.004 |
non-ferrous | ||||
N1 | 60–100 | 325–820 | – | .002–.010 |
high-temp alloys | ||||
S1 | 200 | 65–140 | 65–130 | .002–.004 |
S2 | 250 | 65–90 | 65–90 | .001–.002 |
S3 | 280 | 50–65 | 50–65 | .001–.002 |
S4 | 350 | 30–50 | 30–50 | .001–.002 |
hardened steel | ||||
H1 | 55HRc | 65–140 | 65–140 | .0004–.001 |